Investigation of tritium release and retention in lithium aluminate
1991
Tritium release from lithium aluminate, although previously investigated by both in-reactor and ex-reactor experiments, remains poorly understood. Agreement between experiments is lacking, and the mechanisms responsible for tritium release from lithium aluminate are under debate. In an effort to improve our understanding of the mechanisms of tritium release from lithium ceramics, we have investigated tritium release from pure lithium aluminate and lithium aluminate doped with impurities. The results of these experiments on large grain size material indicate that after anneals at low temperature, a large fraction of the tritium present before the anneal remains in the sample. We have modeled this behavior based on first-order release from three types of sites. At the lowest temperature, the release is dominated by one site, while the tritium in the other sites is retained in the solid. Adding magnesium dopant to the ceramic appears to alter the distribution of tritium between the sites. This addition decreases the fraction of tritium released at 777{degree}C, while increasing the fractions released at 538 and 950{degree}C. 11 refs., 8 figs., 1 tab.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
0
References
2
Citations
NaN
KQI