Investigation of mechanical and electrical properties of Li doped sodium niobate ceramic system

ABSTRACTThe Na0.96Li0.04NbO3 ceramic solid solution was prepared by means of a two-stage hot-pressing technology. The X-ray diffraction analysis showed the formation of a single perovskite phase with an orthorhombic symmetry in the investigated composition. The microstructure and EDS measurements were performed. They confirmed the high purity and the expected qualitative composition. A good homogeneity of the microstructures and a small degree of porosity were observed. The elastic modulus (the Young's modulus E, shear modulus G, and Poisson's ratio ν) of Na0.96Li0.04NbO3 were determined with the use of an ultrasonic method. The electrical properties of Na0.96Li0.04NbO3 ceramics were investigated at the frequency ranging from 0.5 kHz to 200 kHz, and the temperature ranging from room temperature to 750 K. The test sample shows a dielectric dispersion.