Micro-Raman spectroscopy study of the process of microindentation in polymers: Part I Poly(3,3-dimethyl oxetane)

The residual deformation produced by Vickers microindentations in poly(3,3-dimethyl oxetane) (PDMO) was analysed by Raman microspectroscopy. Microstructural variations were observed as the Raman spectra were recorded at different positions along and out of the microindentation. A gradual distribution of the monoclinic and orthorhombic structures arises as the spectra were scanned from the centre to the edge of the impression area. This crystalline variation in PDMO, which reflects the degree of stress present on the surface of the sample, was utilized to obtain information on the distribution of pressure in and around the microindentation