Ca3Co2O6Ce0.8Sm0.2O1.9 composite cathode material for solid oxide fuel cells

Abstract Oxygen-ion transport property greatly affects the electro-catalytic activity of a cathode material in the solid oxide fuel cells. In this work, to enhance the electrochemical activity of hexagonal Ca 3 Co 2 O 6 cathode, fast ion-conductor Ce 0.8 Sm 0.2 O 1.9 is introduced as the second phase, and thus a binary composite is developed, expressed as (1- x )Ca 3 Co 2 O 6 / x Ce 0.8 Sm 0.2 O 1.9 in nominal form. The composites are prepared by one-pot method and X-ray diffraction results reveal that these compositional phases are highly compatible. Analysis of X-ray photoelectron spectroscopy indicates the existence of Co 3+ and Co 2+ mixed valences in the composites. Compared with single-phase Ca 3 Co 2 O 6 , thermal expansion coefficient of the composite is favorably low and matches better with the electrolyte of solid oxide fuel cells. Test of electrical conductivity shows that the composites are comparable to the pure Ca 3 Co 2 O 6 in charge transport capacity. Electrochemical measurements indicate that the x  = 0.5 composite cathode exhibit the lowest area specific resistance and produces the maximum power density. In the electrolyte-supported single cell along with Ni-SDC cermet as anode and pure H 2 gas as fuel, power density peak of 680 mWcm −2 is achieved from the x  = 0.5 composite cathode at 800 °C.