Chemical, mechanical and biological properties of contemporary composite surface sealers.

Abstract Objectives To evaluate the chemical, mechanical, and biological properties of modern composite surface sealers (CSS) having different compositions. Methods The CSS products tested were Biscover LV (BC), Durafinish (DF), G-Coat Plus (GC), and Permaseal (PS). The tests performed were: (A): degree of conversion (DC%) by ATR-FTIR spectroscopy; (B): thickness of O 2 -inhibition layer by transmission optical microscopy; (C): surface hardness, 10 min after irradiation and following 1 week water storage, employing a Vickers indenter (VHN); (D): color (Δ E *) and gloss changes (ΔGU) after toothbrush abrasion, using L * a * b * colorimetry and glossimetry; (E): accelerated wear (GC,PS only) by an OHSU wear simulator plus 3D profilometric analysis, and (F): cytotoxicity testing of aqueous CSS eluents on human gingival fibroblast cultures employing the methyl- 3 H thymidine DNA labeling method. Statistical analyses included 1-way (A, B, Δ E *, ΔGU) and 2-way (C, F) ANOVAs, plus Tukey post hoc tests. Student's t -test was used to evaluate the results of the accelerated wear test ( α  = 0.05 for all). Results The rankings of the statistical significant differences were: (A) PS (64.9) > DF,BC,GC (56.1–53.9) DC%; (B) DF,PS (12.3,9.8) > GC,BC (5.2,4.8) μm; (C): GC (37.6) > BC,DF (32.6,31.1) > PS (26.6) VHN (10 min/dry) and BC,DF (29.3,28.7) > GC(26.5) > PS(21.6) VHN (1w/water), with no significant material/storage condition interaction; (D): no differences were found among GC,DF,BC,PS (0.67–1.11) Δ E *, with all values within the visually acceptable range and PS,BC (32.8,29.4) > GC,DF (19.4,12.9) ΔGU; (E): no differences were found between GC and PS in volume loss (0.10,0.11 mm 3 ), maximum (113.9,130.5 μm) and mean wear depths (30.3,27.5 μm); (F): at 1% v/v concentration, DF showed toxicity (23% vital cells vs 95–102% for others). However, at 5% v/v concentration DF (0%) and BC (9%) were the most toxic, whereas GC (58%) and PS (56%) showed moderate toxicity. Significance Important chemical, mechanical, and biological properties exist among the CSS tested, which may affect their clinical performance.