COEXISTENCE OF SUPERPARAMAGNETIC AND FERROMAGNETIC COMPONENTS IN (CuGa) 1-x Fe x Se 2-x SOLID SOLUTIONS WITH x=0.1, 1/3 and 1/2 ( COEXISTENCIA DE COMPONENTES FERROMAGNÉTICA Y SUPERPARAMAGNÉTICA EN SOLUCIONES SÓLIDAS (CUGA) 1-X FE X SE 2-X CON X=0.1, 1/3 Y 1/2 )

The magnetic behavior of (CuGa) 1-x Fe x Se 2-x solid solutions with compositions x=0.1, 1/3 and 1/2 has been investigated using SQUID techniques. DC magnetic susceptibility was measured in the temperature range 2 < T < 300K using Zero Field Cooling (ZFC) – Field Cooling (FC) protocol. It has been observed that the experimental curves can be analyzed as the sum of two magnetic components, one superparamagnetic and the other one ferromagnetic. The ferromagnetic component persist up to temperatures higher than room temperature making this report the first observation of room temperature ferromagnetism in A I B III C VI 2 compounds doped (or alloyed)with transition metals. El comportamiento magnetico de las soluciones solidas (CuGa) 1-x Fe x Se 2-x con composiciones x=0.1, 1/3 y 1/2 fue investigado por medio de la tecnica de SQUID. Las susceptibilidades DC fueron medidas en el rango de temperatura 2 < T < 300K usando el protocolo Enfriamiento a Campo Zero (ECZ) – Enfriamiento con Campo (EC). Se observo que las curvas experimentales podian ser analizadas como la suma de dos componentes magneticas, una superparamagnetica y otra ferromagnetica. La componente ferromagnetica persiste a temperaturas por arriba de la temperatura ambiente siendo este reporte la primera observacion de ferromagnetismo a temperatura ambiente en compuestos A I B III C VI 2 dopados (o aleados) con metales de transicion.