Irradiation of KU1 and KS-4V substrate SiO2 overcoated Al mirrors
2013
Abstract Previous work on overcoated dielectric mirrors identified several radiation problems; UV–visible reflectivity degradation, unreliability of manufacturers coating specifications, and conversion of SiO coatings to SiO 2 leading to swelling and cracking, and hence possible corrosion during LOCAs (loss of coolant accident). We report the results obtained for gamma and neutron irradiation of prototype mirrors with KU1 and KS-4V high purity silicas replacing the standard Pyrex substrate to overcome the problem of activation due to high impurity content. To avoid the SiO to SiO 2 conversion problem, the Al layer has been overcoated with SiO 2 . The mirrors show high reflectivity (>80%) down to 200 nm. After gamma irradiation at 170 °C in a dry nitrogen atmosphere to 10 MGy, no degradation in reflectivity was observed. They were then neutron irradiated in vacuum at 35 °C to 6.8 × 10 16 n/cm 2 (fast fluence) and reflectivity examined with a specially designed spectrometer system with a remote integrating sphere for hot cell use. Again no degradation in reflectivity was observed.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
4
References
1
Citations
NaN
KQI