Large inverse tunneling magnetoresistance in Co$_2$Cr$_{0.6}$Fe$_{0.4}$Al/MgO/CoFe magnetic tunnel junctions

Magnetic tunnel junctions with the layer sequence Co$_2$Cr$_{0.6}$Fe$_{0.4}$Al/MgO/CoFe were fabricated by magnetron sputtering at room temperature (RT). The samples exhibit a large inverse tunneling magnetoresistance (TMR) effect of up to -66% at RT. The largest value of -84% at 20 K reflects a rather weak influence of temperature. The dependence on the voltage drop shows an unusual behavior with two almost symmetric peaks at $\pm600$ mV with large inverse TMR ratios and small positive values around zero bias.