Effects of Nitrogen Incorporation in HfO2 Grown on InP by Atomic Layer Deposition: An Evolution in Structural, Chemical, and Electrical Characteristics

We investigated the effects of postnitridation on the structural characteristics and interfacial reactions of HfO2 thin films grown on InP by atomic layer deposition (ALD) as a function of film thickness. By postdeposition annealing under NH3 vapor (PDN) at 600 °C, an InN layer formed at the HfO2/InP interface, and ionized NHx was incorporated in the HfO2 film. We demonstrate that structural changes resulting from nitridation of HfO2/InP depend on the film thickness (i.e., a single-crystal interfacial layer of h-InN formed at thin (2 nm) HfO2/InP interfaces, whereas an amorphous InN layer formed at thick (>6 nm) HfO2/InP interfaces). Consequently, the tetragonal structure of HfO2 transformed into a mixture structure of tetragonal and monoclinic because the interfacial InN layer relieved interfacial strain between HfO2 and InP. During postdeposition annealing (PDA) in HfO2/InP at 600 °C, large numbers of oxidation states were generated as a result of interfacial reactions between interdiffused oxygen impur...