Preparation method and use method of modified bentonite environment-friendly formaldehyde removing agent

The invention relates to a modified bentonite environment-friendly formaldehyde removing agent for removing free formaldehyde in urea-formaldehyde glue. A preparation method of the formaldehyde removing agent comprises the following steps of: in parts by weight, crushing 100 parts of calcium bentonite, screening the crushed calcium bentonite through a 200-mesh sieve, adding 2 to 3.5 parts of sodium carbonate into the screened calcium bentonite, mixing uniformly, spraying water of which the weight accounts for 10 percent of that of the calcium bentonite, fully mixing uniformly, sealing the mixture for 24 hours for sodication reaction, and air-drying naturally; and adding 0.5 to 2.5 parts of hydroxyethyl cellulose, 1.5 to 2.5 parts of ammonia chloride and 2.5 to 5 parts of sodium nitrite into 100 parts of a raw material subjected to sodication, crushing the mixture and stirring for 3 hours to obtain powder, and screening the powder through a 300-mesh sieve to obtain formaldehyde removing powder. A use method of the modified bentonite environment-friendly formaldehyde removing agent comprises the following steps of: in parts by weight, adding 10 parts of water into 10 parts of the formaldehyde removing agent, stirring at a high speed for 40 minutes, adding 10 parts of a suspension of the mixture into 90 parts of the urea-formaldehyde glue, raising the temperature to 50 DEG C, fully stirring for 30 minutes, standing for more than 24 hours, and thus fully adsorbing the formaldehyde in the urea-formaldehyde glue. The modified bentonite environment-friendly formaldehyde removing agent has good adsorption effect on the formaldehyde, and cannot influence the performance of the urea-formaldehyde glue.