Investigation of interfacial interaction between uncoated and coated carbon fibres and the magnesium alloy AZ91

Unidirectionally reinforced metal–matrix composites with a fibre volume content between 63 and 68% were processed by squeeze casting using T800 H carbon fibres and the magnesium alloy AZ91. The surface of the fibres was prepared by thermal desizing of the fibres or by deposition of a pyrolytic carbon (pyC) coating. Different interfacial conditions could be identified by transmission electron microscopy (TEM) and the single-fibre push-in test. TEM confirmed the formation of needle-like phases at the fibre surface or, for coated fibres, within the pyrolytic carbon coating. During loading by the Vickers type indenter an intense response was observed for composites of coated fibres and the magnesium alloy. This could by caused by stick–slip effects within the pyrolytic carbon coating.