Determination of Solvent–Polymer and Polymer–Polymer Flory–Huggins Interaction Parameters for Poly(3-hexylthiophene) via Solvent Vapor Swelling
2013
We report the use of solvent vapor swelling of ultrathin polymer films to determine Flory–Huggins solvent–polymer and polymer–polymer interaction parameters (χi–j) for poly(3-hexylthiophene) (P3HT) and polystyrene (PS) over a wide solvent composition range. From the calculated interaction parameters, we constructed a polymer/polymer/solvent phase diagram that was validated experimentally. χtetrahydrofuran–P3HT (1.04 ± 0.04) and χCHCl3–P3HT (0.99 ± 0.01) were determined through swelling of ultrathin P3HT films. Similar experiments using PS films gave χtetrahydrofuran–PS = 0.41 ± 0.02 and χCHCl3–PS = 0.39 ± 0.01, consistent with literature values. As expected, these χi–j parameters indicated that P3HT is less compatible than PS with either solvent. From δPS (17.9 ± 0.2 MPa1/2) and δP3HT (14.8 ± 0.2 MPa1/2), determined through regular solution theory, we calculated χPS–P3HT = 0.48 ± 0.06 at 23 °C. The resulting phase diagram was validated by solution-based transmission measurements of PS/P3HT blends in o-xyl...
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
64
References
73
Citations
NaN
KQI