Influence of Solutocapillary Convection on Macrovoid Defect Formation in Polymeric Membranes

The focus of this research project involved the dry-cast process for polymeric membrane formation, whereby evaporation of solvent from an initially homogeneous polymer/solvent/ nonsolvent solution results in phase separation and the formation of polymer-rich and polymer-lean phases. Under certain conditions the polymer-lean phase gives rise to very large and usually undesirable, tear-drop-shaped pores (size approx. 10 - 50 microns) termed macrovoids (MVs). Although in many cases the presence of MV pores has deleterious effects on membrane performance, there are a number of innovative applications where the presence of such pores is highly desirable. Although researchers have proposed a variety of mechanisms for MV formation over the past three decades, two main hypotheses are currently favored: one asserts that MV growth can be attributed solely to diffusion (the diffusive growth hypothesis), whereas the other states that solutocapillary convection (the SC hypothesis) at the MV interface contributes to growth. The overall goal of this research was to obtain a more comprehensive understanding of the fundamental mechanism of MV growth. This research incorporates a coupled modeling and experimental approach to test a solutocapillary convection hypothesis for the growth of macrovoid pores in polymeric membranes. Specifically, we utilized a modification of the first principles model developed by two of the PIs (ARG and WBK) for dry-cast CA membranes. For the experimental component, two separate and mutually complementary approaches were used to study MV growth. In the first, membranes cast in a zero-g environment aboard the NASA KC-135 aircraft were compared with those cast on the ground to assess the effect of the buoyancy force on membrane morphology and MV size and shape. In the second approach, videomicroscopy flow visualization (VMFV) was utilized to observe MV formation and growth in real time and to assess the effect of surface tension on the MV growth dynamics. As a result of these fundamental studies, our research group advanced a new hypothesis for MV pore development in polymeric membranes.