High heating ability of one-step carbothermal reduction method of Fe3O4 nanoparticles upon magnetic field

Abstract Induction heating Fe3O4 nanoparticles are commonly used in magnetic hyperthermia. For the best comprehensive efficiency, particles are needed which possess the highest possible heating rates/specific absorption rate when being exposed to a magnetic field. In this paper, a fail one-step carbothermal reduction method for magnetic nanoparticles is optimized towards yielding Fe3O4 nanoparticles with small-size (6.5 ± 2 nm), strong magnetism (90.2 emu·g−1), and high heating rates. The parameters of alternating magnetic field are studied in depth to understand how to produce the best heating rates. Hyperthermia measurements were performed under an alternating magnetic field with a frequency of 165.3 kHz, 245.6 kHz and calculated the specific absorption rate. The optimum specific absorption rate is 43.5 W·g−1 at 15 mT and 245.6 kHz. The maximum intrinsic loss power (ILP) value is 3.8 nHm2·kg−1.