LEVELS OF TAPER CORROSION AND WEAR IN 50 RETRIEVED ASR XL METAL-ON-METAL HIP COMPONENTS

The articulating surface replacement (ASR) XL stemmed total hip replacement and ASR resurfacing hip systems were recalled by DePuy due to a high prevalence of early failure. The ASR XL has a greater failure rate than the ASR resurfacing, which has been increasingly attributed to wear and corrosion at the taper interface between the female taper surface of the femoral head and the male taper (trunnion) of the femoral stem. The aim of this study was to quantify the prevalence and severity of taper corrosion in retrieved ASR XL hip components.A peer-reviewed subjective corrosion scoring system was used to quantify corrosion in a consecutive series of the 50 ASR XL hip components (head components – n=44; femoral stems – n=6) at our retrieval centre. Bearing surface wear (femoral head and acetabular cup combined) was quantified and a value of <5 microns was defined as low-wearing. Subsequent profilometry analysis was undertaken in the low-wearing hips to quantify material loss from the taper interface.90% of c...