Tungsten Trioxide/Zinc Tungstate Bilayers: Electrochromic Behaviors, Energy Storage and Electron Transfer
2014
Abstract Pair-sequentially spin-coated tungsten trioxide (WO 3 ) and zinc tungstate (ZnWO 4 ) bilayer films onto indium tin oxide (ITO) coated glass slides have been prepared via sol-gel methods followed by annealing. The bilayers (ZnWO 4 /WO 3 denoting the bilayer film with the inner layer of ZnWO 4 and the outer layer of WO 3 on the ITO while WO 3 /ZnWO 4 standing for the bilayer film with the inner layer of WO 3 and the outer layer of ZnWO 4 on the ITO) exhibit integrated functions of electrochromic and energy storage behaviors as indicated by the in situ spectroelectrochemistry and cyclic voltammetry (CV) results. Accordingly, blue color was observed for the bilayer films at -1 V in 0.5 M H 2 SO 4 solution. An areal capacitance of 140 and 230 μF/cm 2 was obtained for the ZnWO 4 /WO 3 , and WO 3 /ZnWO 4 film, respectively, at a scan rate of 0.05 V/s in the CV measurements. The CV results also unveiled the electron transfer behavior between the semiconductor films in the oxidation process, suggesting a sequence-dependent electrochemical response in the bilayer films. Meanwhile, methylene blue (MB) was used as an indicator to study the electron transfer phenomenon during the reduction process at negative potentials of -0.4 and -0.8 V, in 0.5 M Na 2 SO 4 . The results indicated that the electrons transfer across the bilayers was enhanced at more negative potentials.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
60
References
75
Citations
NaN
KQI