10 μm minority-carrier diffusion lengths in Si wires synthesized by Cu-catalyzed vapor-liquid-solid growth
2009
The effective electron minority-carrier diffusion length, L_(n,eff), for 2.0 µm diameter Si wires that were synthesized by Cu-catalyzed vapor-liquid-solid growth was measured by scanning photocurrent microscopy. In dark, ambient conditions, L_(n,eff) was limited by surface recombination to a value of ≤ 0.7 µm. However, a value of L_(n,eff) = 10.5±1 µm was measured under broad-area illumination in low-level injection. The relatively long minority-carrier diffusion length observed under illumination is consistent with an increased surface passivation resulting from filling of the surface states of the Si wires by photogenerated carriers. These relatively large L_(n,eff) values have important implications for the design of high-efficiency, radial-junction photovoltaic cells from arrays of Si wires synthesized by metal-catalyzed growth processes.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
14
References
81
Citations
NaN
KQI