Correlation between Microstructure and Magnetic Properties in FeNdB Permanent Magnets Doped with Al2O3

Two-phase sintered magnets composed of the hard magnetic Fe14Nd2B and a Nd-rich nonmagnetic phase are produced doping the master alloy of Fe73.5Nd20B6.5 with 1.48 mass% Al2O3. Measuring the temperature dependence of the coercive field in these sintered magnets the effect of the microstructure on the coercive field can be quantitatively analysed. In particular it can be shown that with increasing grain size the demagnetization effects originating from local stray fields increase whereas the surface quality of the grains is improved. Es werden gesinterte Zwei-Phasen-Magnete, zusammengesetzt aus der magnetisch harten Fe14Nd2B-und einer Nd-reichen nichtmagnetischen Phase, hergestellt indem die Grundlegierung Fe73.5Nd20B6,5 mit 1,48 Massen% Al2O3 dotiert wird. Durch Messung der Temperaturabhangigkeit des Koerzitivfeldes in diesen gesinterten Magneten last sich der Einflus der Mikrostruktur auf das Koerzitivfeld quantitativ analysieren. Insbesondere kann gezeigt werden, das mit wachsender Korngrose die Entmagnetisierungseffekte, die aus lokalen Streufeldern herruhren, wachsen wahrend die Oberflachenqualitat der Korner verbessert wird.