Detection system for inclusion defects in hot-rolled steel plates using MFLT with two different magnetizing strengths

Recently, steel can manufacturing requires higher quality because otherwise minute non-metallic inclusions in thin sheets cause cracks and result in a burst during pressurization after the pressing process. Quality testing systems have already been installed in the final process in steel plants, but if there were another inspection in an earlier step, for example, at the hot strip mill, the mass manufacture of nonconforming products could be avoided and maintaining quality control would be more efficient. In order to detect inclusion defects in hot-rolled steel plates, the authors developed a new technique for MFLT (Magnetic Flux Leakage Testing) using different magnetizing forces. According to an analysis of the noise factors in MFLT, it was found that the signals generated from the scale layer on a steel surface are dominant. A different magnetizing force method is the used to decrease this overpowering noise level in MFLT. In this paper, it was confirmed that inclusions larger than 160μm in diameter an...