Crack-healing behavior and static fatigue strength of Si3N4/SiC ceramics held under stress at temperature (800, 900, 1000 °C)
2003
Abstract Si 3 N 4 /SiC composite ceramics were sintered and subjected to three-point bending. A semi-elliptical surface crack of 100 μm in surface length was introduced on each specimen. The pre-crack was healed under constant bending stress of 210 MPa at 800, 900 and 1000 °C. Applied stress of 210 MPa is ∼70% of the bending strength of pre-cracked specimen. Bending strength and static fatigue strength of crack-healed specimens were systematically investigated at each crack-healing temperature. The bending strength of crack healed specimen showed almost the same value as smooth specimen. Thus, Si 3 N 4 /SiC composite ceramics could heal a crack even under constant bending stress of 210 MPa at 800, 900 and 1000 °C. Moreover, crack-healed zone had quite high static fatigue limit at each crack-healing temperature. These conclusions indicate that Si 3 N 4 /SiC composite ceramics has an ability to heal a crack under service condition, i.e. high temperature and applied stress.
Keywords:
- Correction
- Source
- Cite
- Save
- Machine Reading By IdeaReader
22
References
34
Citations
NaN
KQI