Characterization of the Interactions of vapour phase inhibitors on metal surfaces by ellipsometry

The interaction of dicyclohexyl ammonium nitrite (DICHAN) and dicyclohexylamine (DICHAMIN) on substrates of pure iron and platinum were investigated by ellipsometry. The initial immersion phase (≤ 100 min) under isothermal conditions (20°C) in air of relative humidity (RH) = 0 or (RH) = 100% was investigated. It is shown, that DICHAN is intensively adsorbed on the primary oxide layer of iron materials and causes effective hydrophobing. DICHAMIN to a lower extent decreases the adsorbability of water and when influenced by air of (RH) = 0%, it is completely desorbed. On the basis of the results presented, the actual views on the active principles of vapour phase inhibitors of the iron materials' atmospheric corrosion are defined. Charakterisierung der Wechselwirkungen von Dampfphaseninhibitoren auf Metalloberflachen durch Ellipsometrie Die Wechselwirkungen von Dicyclohexylammoniumnitrit (DICHAN) und Dicyclohexylamin (DICHAMIN) an Substraten aus reinem Eisen und Platin wurden mittels Ellipsometrie untersucht. Erfast wurde die Anfangsphase der Immersion (≤ 100 min) unter isothermen Bedingungen (20°C) in Luft der relativen Feuchte (RH) = 0 oder (RH) = 100%. Es wird gezeigt, das DICHAN an der Primaroxidschicht der Eisenproben intensiv adsorbiert wird und eine wirkungsvolle Hydrophobierung bedingt. Das DICHAMIN setzt die Adsorbierbarkeit von Wasser weniger stark herab und wird bei Einwirkung von Luft mit (RH) = 0% vollstandig desorbiert. Auf der Basis der vorgestellten Ergebnisse werden die bisherigen Ansichten zum Wirkprinzip von Dampfphaseninhibitoren der atmospharischen Korrosion von Eisenwerkstoffen prazisiert.