Physical, mechanical, chemical and thermal properties of nanoscale graphene oxide-poly methylmethacrylate composites:

The purpose of this laboratory study was to formulate and characterize the graphene oxide-poly(methyl methacrylate) resin composite with an intended use as bone cement. Graphene oxide was fabricated through ultrasonication route. The autopolymerization resin (Eco Cryl Cold, Protechno, Vilamalla Girona, Spain) was used to prepare the specimens of required dimensions for different testing parameters. The control group (C-group) was prepared as such. However, for GO1-group, 0.024 wt/wt.-% of graphene oxide was incorporated in a resin matrix and GO2-group was a composite with 0.048 wt/wt.-% of graphene oxide in a resin matrix. TEM examination of graphene oxide sheets demonstrated them in the range of ∼500 nm to ∼2 µm. The mechanical properties were characterized using three-point bending and wear resistance, while material properties were assessed through transmission electron microscope, scanning electron microscopy, Fourier-transform infrared spectroscopy, Raman spectroscopy, X-ray diffraction, differential...