CHARACTERIZATION AND PERFORMANCE OF DUPLEX-COATINGS ON Cr-V COLD WORK TOOL STEEL

Specimens made of Vanadis 6 steel were heat treated, plasma nitrided and coated with Cr 2 N. The microstructure, phase constitution and mechanical properties of plasma nitrided areas and duplex-coatings have been investigated using the light microscopy, scanning electron microscopy, X-ray diffraction and microhardness measurements. The adhesion of the coatings and the wear performance were studied using the scratch test and ring-on-plate tribological testing. Worn surfaces were examined by scanning electron microscopy. Nitrided areas formed at lower temperature were free of compound “white” layer while hose developed at higher temperatures contained as the white layer so the nitrided network. Significant increase in substrate hardness was detected due to the nitriding. Beneficial effect of the nitriding on the adhesion of Cr 2 N coatings was clearly determined whereas the extent in improvement of the adhesion depends on the presence/no presence of “white” layer on the surface. The extent of beneficial effect of plasma nitriding on the wear performance follows the impact of the constitution of nitrided areas on the adhesion. The amelioration of wear performance of Cr 2 N coatings can be attributed to the supporting effect of hard nitrided intermediate region, which provides excellent resistance of the substrate against plastic deformation, under heavy loading in particular. Practical testing demonstrated many times prolonged service-time of duplex-treated tools for sheet metal working.