Mineral trioxide aggregate

Mineral trioxide aggregate (MTA) was developed for use as a dental root repair material by Mahmoud Torabinejad. It is formulated from commercial Portland cement, combined with bismuth oxide powder for radiopacity. MTA is used for creating apical plugs during apexification, repairing root perforations during root canal therapy, and treating internal root resorption. This can be used for root-end filling material and as pulp capping material. Originally, MTA was dark gray in color, but white versions have been on the market since 2002. Mineral trioxide aggregate (MTA) was developed for use as a dental root repair material by Mahmoud Torabinejad. It is formulated from commercial Portland cement, combined with bismuth oxide powder for radiopacity. MTA is used for creating apical plugs during apexification, repairing root perforations during root canal therapy, and treating internal root resorption. This can be used for root-end filling material and as pulp capping material. Originally, MTA was dark gray in color, but white versions have been on the market since 2002. Portland cement is a term applied to a class of materials covering a range of compositions (between silica alumina and calcia). The composition, fineness, setting time and strength of Portland cement are not controlled or guaranteed. Portland cement is an unsuitable substitute for MTA based on several characteristics that are essential to the performance: freedom from heavy metals, dimensional stability and fineness. The FDA requires dental materials to have high purity and be lead and arsenic-free, unlike commercial Portland cement. MTA is composed of tricalcium silicate, dicalcium silicate, tricalcium aluminate, tetracalcium aluminoferrite, calcium sulfate, and bismuth oxide.The later 4 phases vary among the commercial products available. Newly developed fast-set MTAs were developed by Pozzolan Cement or Zeolite Cement. These were used by pozzolanic reaction. Pozzolan Cement is a mineral aggregate with watery calcium silicate hydration.