Shielded metal arc welding

Shielded metal arc welding (SMAW), also known as manual metal arc welding (MMA or MMAW), flux shielded arc welding or informally as stick welding, is a manual arc welding process that uses a consumable electrode covered with a flux to lay the weld. An electric current, in the form of either alternating current or direct current from a welding power supply, is used to form an electric arc between the electrode and the metals to be joined. The workpiece and the electrode melts forming a pool of molten metal (weld pool) that cools to form a joint. As the weld is laid, the flux coating of the electrode disintegrates, giving off vapors that serve as a shielding gas and providing a layer of slag, both of which protect the weld area from atmospheric contamination. Because of the versatility of the process and the simplicity of its equipment and operation, shielded metal arc welding is one of the world's first and most popular welding processes. It dominates other welding processes in the maintenance and repair industry, and though flux-cored arc welding is growing in popularity, SMAW continues to be used extensively in the construction of heavy steel structures and in industrial fabrication. The process is used primarily to weld iron and steels (including stainless steel) but aluminium, nickel and copper alloys can also be welded with this method. After the discovery of the short pulsed electric arc in 1800 by Humphry Davy and of the continuous electric arc in 1802 by Vasily Petrov, there was little development in electrical welding until Auguste de Méritens developed a carbon arc torch that was patented in 1881. In 1885, Nikolay Benardos and Stanisław Olszewski developed carbon arc welding, obtaining American patents from 1887 showing a rudimentary electrode holder. In 1888, the consumable metal electrode was invented by Nikolay Slavyanov. Later in 1890, C. L. Coffin received U.S. Patent 428,459 for his arc welding method that utilized a metal electrode. The process, like SMAW, deposited melted electrode metal into the weld as filler. Around 1900, A. P. Strohmenger and Oscar Kjellberg released the first coated electrodes. Strohmenger used clay and lime coating to stabilize the arc, while Kjellberg dipped iron wire into mixtures of carbonates and silicates to coat the electrode. In 1912, Strohmenger released a heavily coated electrode, but high cost and complex production methods prevented these early electrodes from gaining popularity. In 1927, the development of an extrusion process reduced the cost of coating electrodes while allowing manufacturers to produce more complex coating mixtures designed for specific applications. In the 1950s, manufacturers introduced iron powder into the flux coating, making it possible to increase the welding speed. In 1938 K. K. Madsen described an automated variation of SMAW, now known as gravity welding. It briefly gained popularity in the 1960s after receiving publicity for its use in Japanese shipyards though today its applications are limited. Another little used variation of the process, known as firecracker welding, was developed around the same time by George Hafergut in Austria. In 1964 laser welding was developed in Bell Laboratory with the intention of using this technology as a communication tool. Due to the large force of energy coupled with the small area of focus, this laser became a powerful heat source for cutting and tooling. To strike the electric arc, the electrode is brought into contact with the workpiece by a very light touch of the electrode to the base metal. The electrode is then pulled back slightly. This initiates the arc and thus the melting of the workpiece and the consumable electrode, and causes droplets of the electrode to be passed from the electrode to the weld pool. Striking an arc, which varies widely based upon electrode and workpiece composition, can be the hardest skill for beginners. The orientation of the electrode to workpiece is where most stumble, if the electrode is held at a perpendicular angle to the workpiece the tip will likely stick to the metal which will fuse the electrode to the workpiece which will cause it to heat up very rapidly. The tip of the electrode needs to be at a lower angle to the workpiece, which allows the weld pool to flow out of the arc. As the electrode melts, the flux covering disintegrates, giving off shielding gases that protect the weld area from oxygen and other atmospheric gases. In addition, the flux provides molten slag which covers the filler metal as it travels from the electrode to the weld pool. Once part of the weld pool, the slag floats to the surface and protects the weld from contamination as it solidifies. Once hardened, it must be chipped away to reveal the finished weld. As welding progresses and the electrode melts, the welder must periodically stop welding to remove the remaining electrode stub and insert a new electrode into the electrode holder. This activity, combined with chipping away the slag, reduces the amount of time that the welder can spend laying the weld, making SMAW one of the least efficient welding processes. In general, the operator factor, or the percentage of operator's time spent laying weld, is approximately 25%.