Exchange bias

Exchange bias or exchange anisotropy occurs in bilayers (or multilayers) of magnetic materials where the hard magnetization behavior of an antiferromagnetic thin film causes a shift in the soft magnetization curve of a ferromagnetic film. The exchange bias phenomenon is of tremendous utility in magnetic recording, where it is used to pin the state of the readback heads of hard disk drives at exactly their point of maximum sensitivity; hence the term 'bias.' Exchange bias or exchange anisotropy occurs in bilayers (or multilayers) of magnetic materials where the hard magnetization behavior of an antiferromagnetic thin film causes a shift in the soft magnetization curve of a ferromagnetic film. The exchange bias phenomenon is of tremendous utility in magnetic recording, where it is used to pin the state of the readback heads of hard disk drives at exactly their point of maximum sensitivity; hence the term 'bias.' The essential physics underlying the phenomenon is the exchange interaction between the antiferromagnet and ferromagnet at their interface. Since antiferromagnets have a small or no net magnetization, their spin orientation is only weakly influenced by an externally applied magnetic field. A soft ferromagnetic film which is strongly exchange-coupled to the antiferromagnet will have its interfacial spins pinned. Reversal of the ferromagnet's moment will have an added energetic cost corresponding to the energy necessary to create a Néel domain wall within the antiferromagnetic film. The added energy term implies a shift in the switching field of the ferromagnet. Thus the magnetization curve of an exchange-biased ferromagnetic film looks like that of the normal ferromagnet except that is shifted away from the H=0 axis by an amount Hb. In most well-studied ferromagnet/antiferromagnet bilayers, the Curie temperature of the ferromagnet is larger than the Néel temperature TN of the antiferromagnet. This inequality means that the direction of the exchange bias can be set by cooling through TN in the presence of an applied magnetic field. The moment of the magnetically ordered ferromagnet will apply an effective field to the antiferromagnet as it orders, breaking the symmetry and influencing the formation of domains.