This study aims to evaluate the quality of tensile testing conducted at the Mechanical Engineering Laboratory of Politeknik Negeri Medan. Based on the results of attribute inspection, there were 42 units of material defects with a value of 0.124260355. The Upper Control Limit (UCL) was 0.415734865, and the Lower Control Limit (LCL) was 0.0167214 or 0. The subsequent check sheet showed that 34 test specimens did not meet the standard. The value was 0.0100591716, the UCL was 0.03631557869, and the LCL was 0.00362 or 0. The next check sheet revealed 25 failed tests with a value of 0.0073964497, a UCL of 0.0299413849, and an LCL of -0.0151484 or 0. This study aims to evaluate the quality of tensile testing conducted at the Mechanical Engineering Laboratory of Politeknik Negeri Medan. Based on the results of attribute inspection, there were 42 units of material defects with a value of 0.124260355. The Upper Control Limit (UCL) was 0.415734865, and the Lower Control Limit (LCL) was 0.0167214 or 0. The subsequent check sheet showed that 34 test specimens did not meet the standard. The value was 0.0100591716, the UCL was 0.03631557869, and the LCL was 0.00362 or 0. The next check sheet revealed 25 failed tests with a value of 0.0073964497, a UCL of 0.0299413849, and an LCL of -0.0151484 or 0.
Serat dan ampas kelapa banyak dihasilkan oleh pedagang kelapa dan industry kelapa. Limbah serat kelapa tidak berbahaya karena organic dan bisa terurai. Akan tetapi limbah kelapa menjadi masalah karena kapasitas yang besar dan menjadi sampah yang kurang termanfaatkan. Atas dasar pertimbangan tersebut maka penelitan ini bertujuan untuk memanfaatkan serat sabuk kelapa sebagai salah satu solusi yang bisa digunakan sebagai new material bagi masyarakat dan industry. Penelitan ini dilaksanakan di Labolatorium Teknik Mesin Politeknik Negeri Medan dengan menggunakan mesin computer servo universal tensile machine dengan kapasitas maksimum mesin 100000 N. Matriks yang digunakan pada penelitian ini adalah resin polister yang disusun dengan serat dengan pertimbangan massa, dimensi dan diameter yang sama yang secara kontiniyu, acak dan terputus-putus. Sampel tersebut dibuat dengan komposisi fraksi volume yaitu (10:90) %, (20:80) %, (30:70) %, (40:60) %, dan (50:50) %. Matriks 50:50 % memiliki stress, strain dan modulus yang tertinggi pada pengujian kali ini. stress sebesar 14,98 MPa, strain 2,00%, beban 12.251 N dan modulus young sebesar 7,49 MPa.
Abstrak. Penelitian ini bertujuan untuk mengetahui sifat-sifat mekanis material dari plat baja ST 37 melalui Brinell hardness Test. Metode yang digunakan pada penelitan ini adalah eksperimen dengan mempersiapkan sampel pengujian dengan standart ASTM E-10. Penelitian ini dilaksanakan di Labolatorium Teknik Mesin Politeknik Negeri Medan. Hasil yang diperoleh pada pengujian pertama nilai HB sebesar 214,62 jejak penekanan 0.37 dan beban 50Kgf. Pada pengujian kedua mengalami penurunan nilai kekerasan, nilai HB yang diperoleh 45,86 dengan jejak penekanan 0.48 dan beban sebesar 50 Kgf. Hasil pengujian ketiga nilai HB sebesar 188,052, jejak penekanan 0,66 dengan beban 59 Kgf. Nilai HB pada pengujian keempat mengalami kenaikan yaitu 113,776 dengan pembebanan 59 Kgf dan jejak penekanan 0,76. Selanjutnya pengujian yang kelima sekaligus pengujian terakhir pada penelitan ini juga mengalami peningkatan nilai kekerasan HB, akan tetapi pengujian ini tidak lebih besar dari pengujian yang pertama, nilai HB yang diperoleh hanya sebesar 90.92 dengan nilai penekanan 1,03 dan beban sebesar 50 Kgf.
The aim of PMKM is to provide training and assistance regarding computer-based technical drawing (AutoCad) which is useful for increasing students' competence in drawing. Training and assistance in computer-based technical drawing (Auto Cad) which is useful for increasing students' competence in technical drawing as a preparation for students to enter the world of work and entrepreneurship for vocational school graduates. The method used to resolve the problems that occurred was to use a survey method at SMK 1 Raksana Medan to obtain PMKM data, then the PMKM team formulated training materials, created a training implementation schedule related to time, arranged instructors who would provide training, created activity evaluation designs. The results of implementing PMKM are: Students understand the basic introduction to using AutoCad and the basic commands used for drawing, especially drawing machine components.
This research is impact testing using the Charpy and Izod methods, temperature variations of 1500 C, 2500 C and raw material as the research variable. The results of the Charpy test with a variation of 150 0C obtained a maximum absorbed energy of 97.65 J, with an impact value of 0.222 J/mm2. Then the maximum energy absorbed through testing at a temperature of 2500C is 78.28 Joules and the impact value is 0.177 J/mm2. Furthermore, the raw material test results showed that the maximum energy absorbed was 145.96 J with an impact value of 0.330 J/mm2. Izod testing with a temperature of 1500C obtained a maximum absorbed energy of 60.94 J with an impact value of 0.101 J/mm2. Furthermore, the maximum energy absorbed at a temperature of 2500C is 36.83 Joules and the impact value is 0.061 J/mm2. The raw material test results show that the maximum energy that can be absorbed is 80.53 J with an impact price of 0.133 J/mm2
One of the most frequently used methods of material testing is hardness testing. The aim of conducting research on material hardness is to determine the hardness value of the material specimens tested, namely ST 37 steel plate and aluminum plate. The test method is to use the Brinell hardness test where the values obtained during testing are from the force load, indenter diameter and pressure trace diameter and the pressure time that has been determined. By using testing tools such as hardness tester, mechanical caliper, indenter, flat file, stopwatch. And the materials used are ST 37 steel plate, aluminum plate and sandpaper. From the test results obtained we can calculate the Brinell hardness value of the test material. The value from the calculation of test data where the highest hardness value using the Brinell method (BHN) for ST 37 steel plate material is 256.992. Meanwhile, the highest hardness value using the Brinell method (BHN) for aluminum plate material is 55,182.
In recent times, many studies have been carried out on desalination systems in areas that have difficulty in obtaining clean water sources. Desalination is a method used to distill salt water or brackish water into clean water using solar power as its energy source. This desalination process is a practical alternative that can be used to offer renewable energy sources that are used to produce clean water. To perform energy analysis, the first law of thermodynamics is used as a basis. This study aims to obtain the results of the amount of energy obtained from the solar desalination system and to determine the factors that greatly affect the amount of energy obtained from the system for evaporating water. The method used in this research is an experiment by testing a solar desalination device for eight days. The results show that the highest thermal energy produced is 8.98 kWh and the lowest is 1.56 kWh, and the factors that influence the amount of thermal energy are the heat transfer coefficient and the amount of distilled water produced by the system.
Alignment adalah salah satu teknik yang digunakan untuk memelihara komponen mesin yang berputar atau mentransfer daya sehingga dapat beroperasi seefektif mungkin dan mencegah kerusakan pada komponen mesin lainnya dari kesalahan yang dibuat selama pemasangan atau pemeliharaan. Alignment merupakan kegiatan perawatan yang banyak dilakukan pada mesin-mesin di industri maupun mesin-mesin yang ada di lingkungan Politeknik Industri Logam Morowali khususnya di Prodi Teknik Perawatan Mesin, kompetensi alignment pada roda gigi dan bantalan/bearing sangat dibutuhkan bagi calon mekanik di industri. Pembuatan alat ini bertujuan untuk sebagai alat simulasi pembelajaran alignment agar mencapai kelurusan dan sentrisitas antara dua poros yang berputar (penggerak dan poros yang digerakkan) untuk mencegah gesekan, getaran, dan masalah lain yang dapat mengurangi masa pakai alat dan, tentu saja, meningkatkan biaya pengeluaran untuk perbaikan atau penggantian alat berat. Proses perancangan alat alignment ini menggunakan metode penggerak berupa sprocket dan rantai dimana penghubung antara motor penggerak dengan poros yang akan digerakan yaitu menggunakan metode sprocket dan rantai. Dalam penelitian ini berfungsi untuk membantu menghasilkan rancangan dengan mempertimbangkan prespektif pengguna, sehingga hasil rancangan dapat bermanfaat secara efektif. Dari hasil uji coba alat setting alignment roda gigi dapat berfungsi dengan baik dengan bantuan inverter sehingga putaran motor dapat direduksi dan dapat dikontrol sesuai dengan ketentuan yang diinginkan. Alat setting alignment sebelumnya memiliki RPM: 1450.8 dan untuk alat setting alignment yang dibuat memiliki RPM: 1455.7 dengan frequency 50 Hz sehingga dapat disimpulkan alat tersebut dapat digunakan untuk praktikum pada laboratorium perbaikan dan pemeliharaan mesin.
Penggunaan material yang bersumber dari alam menjadi trend dalam dekade terakhir. Salah satunya yaitu penggunaan material biokomposit untuk pembuatan plastik yang ramah lingkungan. Biokomposit PVA pada riset ini, mengembangkan phytoplankton (PP) sebagai tambahan yang memperbaiki sifat hidrofobik PVA. Tujuan riset ini untuk mengetahui sifat hidrofobik dari Phytoplankton serta potensi kegunaannya dalam pembuatan biokomposit plastik yang ramah lingkungan dengan metode pengujian sifat hidrofobik menggunak pengujian Fourier transform Infrared Spectroscopy (FTIR). Pada penelitian ini dilakukan pembuatan biokomposit dengan penambahan Phytoplankton meliputi PVA murni, 0,6 gr, 0,8 gr dan 1 gr. Gugus fungsional pada panjang gelombang sekitar 3301 cm-1, 2925 cm-1, 1439 cm-1 diindikasikan adanya peregangan O-H, peregangan C-H dan deformasi C-H. Penambahan Phytoplankton pada PVA membuat gugus O-H bebas berkurang dalam film biokomposit. Pada penambahan 1 gr Phytoplankton kedalam PVA murni, nilai transmitansi gugus O-H bebas meningkat dari 87,4 % hingga 94,6 %. jumlah O-H bebas berkurang dikarenakan Phytoplankton yang terdispersi dengan baik pada matriks dan kedua material membentuk ikatan hidogen yang cukup baik antara Phytoplankton dan matriks.
Each material has a different type of toughness, such as the type of 10 mm nako iron material. In use, the material can be damaged. One of the factors that can cause damage is temperature. To find out how the effect of temperature on the material, one of the material tests was carried out, namely impact testing with the charpy method. This impact test is carried out on materials that have been given different temperature variations. There are 6 test specimens used at different temperatures. As a result, at the highest temperature, namely at 31 oC, the absorbed energy is 180.84 J with an impact price of 180.84 J/cm2 and at a low temperature, namely at 4 oC, the absorbed energy is 256.8 J with an impact price of 256 .8 J/cm2.