Abstract This study presents incremental finite element computations of creep‐fatigue crack growth in Alloy 718 at in air. Alloy 718 is representative of creep‐brittle materials, in which viscoplastic deformation is restricted near the tip of a growing crack. The computations predict crack growth using a unique combination of an irreversible cohesive zone formulation and a strain gradient viscoplastic material model based on the Kocks–Mecking formulation. Cohesive zone damage parameters are estimated using sustained loading and constant‐amplitude cyclic loading experiments. Computations of crack extension under three different waveforms containing overloads all predict post‐overload retardation. The amount of retardation depends strongly on the overload ratio, consistent with experiments in the literature using similar waveforms. Analysis of the crack‐tip fields demonstrates retardation is associated with unloading in the highly deformed material near the advancing crack tip. Dynamic recovery and geometrically necessary dislocations are shown to significantly influence post‐overload crack extension.
An important challenge in predicting fatigue and creep crack growth is describing crack growth rates under transient conditions. Transient conditions occur when similitude is violated at the crack tip due to the applied loads or material behavior. Crack growth models like the Paris law, valid for homogeneous materials under constant-amplitude cyclic loading or sustained loading, no longer apply. Transient crack growth rates are strongly influenced by changes in plastic deformation at the crack tip. Activation of time-dependent damage and viscoplastic deformation at high temperatures further complicates the problem.This thesis advances knowledge and predictive capabilities for transient creep and fatigue crack growth in metals, with specific applications to two technologically-relevant nickel-base superalloys. Finite element computations of crack growth following overloads and in multilayered materials are conducted. Crack extension is an outcome of the boundary value problem through an irreversible cohesive zone model and its interaction with plasticity and viscoplasticity in the bulk material.First, fatigue crack growth in rate-independent materials is analyzed. The plasticity formulation considers both plastic strain and gradients of plastic strain, which produce hardening beyond that predicted by classical plasticity models. The computations demonstrate that hardening due to plastic strain gradients plays a significant role in transient fatigue crack growth following overloads. Fatigue crack growth transients associated with material inhomogeneity are studied through the case of a crack growing toward interfaces between plastically dissimilar materials. Interactions between the interface strength and the yield strength mismatch are found to govern crack growth rates near the interface. Hardening due to plastic strain gradients is important for finding the critical conditions associated with crack bifurcation at an interface and penetration through an interlayer.Subsequently, crack growth in rate-dependent materials is analyzed. For materials characterized by power-law viscoplasticity, fatigue crack growth rates following overloads are found to depend strongly on the material rate sensitivity. The computations predict a transition from acceleration- to retardation-dominated post-overload crack growth as the rate sensitivity decreases. The predicted post-overload crack growth rates show good agreement with high-temperature experimentally-measured trends for Alloy 617, a solid solution strengthened nickel-base superalloy proposed for use in next-generation nuclear power plants. The results demonstrate why Alloy 617 behaves in a relatively brittle manner following overloads despite being characterized as a creep-ductile material. Crack growth is also studied in materials where rate dependence is captured through time-dependent damage and dislocation storage and dynamic recovery processes. This approach is relevant for high-strength creep-brittle materials, in which the viscoplastic zone grows with the advancing crack. The computations predict crack growth retardation for several loading waveforms containing overloads. The amount of retardation depends strongly on the overload ratio and subsequent unloading ahead of the crack tip. The predicted post-overload crack extension shows good agreement with high-temperature experimentally-measured trends for Alloy 718, a precipitation-hardened nickel-base superalloy used in turbine engines and power generation applications. The results demonstrate why Alloy 718 behaves in a ductile manner following overloads, despite being characterized as a creep-brittle material.
This paper reports on a system using a Digital Micromirror Device (DMD) to modulate a near-infrared laser source spatially and temporally. The DMD can produce an arbitrary heat source varying both spatially and temporally over the target. When the thermal response of the target surface is recorded using a thermal imager, this provides new possibilities in subsurface defect detection, partially with regard to features whose orientation does not allow them to be resolved using conventional thermographic inspection techniques. In this respect it is similar to conventional focused spot detection approaches; however, the DMD allows the signal to be frequency/phase multiplexed which provides for simultaneous interrogation over a large area. The parallel nature of the process permits a longer inspection time at each point which has signal-to-noise benefits. Preliminary experiments demonstrating the multiplexing approach are presented using a low-cost thermal imager. A NIR laser is spatially and temporary modulated to generated multiple thermal line sources on the surface of a composite circuit board. The infrared response is demodulated point-by-point at each drive frequency. This permits the thermal response from each line source to be resolved individually. Beyond damage detection the approach also has applications to system identification. Initial limitations due to the test setup are discussed along with future system improvements.
