We report the room temperature operation of 8–12 μm InSbBi long-wavelength infrared photodetectors. The InSbBi/InSb heterostructures were grown on semi-insulating GaAs (001) substrates by low pressure metalorganic chemical vapor deposition. The voltage responsivity at 10.6 μm was about 1.9 mV/W at room temperature and the corresponding Johnson noise limited detectivity was estimated to be about 1.2×106 cmHz1/2/W. The carrier lifetime derived from the voltage dependent responsivity measurements was about 0.7 ns.